A series of single-edge notched tension (SENT or SE(T)) and single-edge notched bend (SENB or SE(B)) testing was carried out at −15 °C using B × B specimens machined from two API X70 large diameter pipeline girth welds. An initial notch was placed either on the heat-affected zone (HAZ) or the weld metal center from the outer diameter side of pipe to simulate a circumferential surface flaw. SE(T) and SE(B) tests were performed according to the CANMET procedure and ASTM E1820, respectively. For all HAZ SE(B) specimens machined from one pipe, ductile cracks initially propagated away from the fusion line and toward the base metal side due to asymmetric deformation, and then pop-in (i.e., the initiation and arrest of a brittle crack) occurred after ductile crack growth of approximately 1 mm, where the crack reached around the intercritical heat-affected zone. HAZ SE(T) specimens also showed that the ductile crack propagation deviated toward the base metal side, but an unstable brittle crack extension was not observed from any SE(T) specimens as opposed to SE(B) specimens. None of the weld metal SE(T) and SE(B) specimens showed pop-in or brittle fracture at −15 °C or room temperature. The difference in test results, for the same material, is associated with the different constraint levels in the two loading modes, taking into account that pop-ins were triggered in high-constraint SE(B) tests, while it was not the case for low-constraint SE(T) tests.
Effects of Loading Mode on Brittle Fracture of X70 Pipe Girth Welds
Contributed by the Pressure Vessel and Piping Division of ASME for publication in the JOURNAL OF PRESSURE VESSEL TECHNOLOGY. Manuscript received August 16, 2016; final manuscript received November 8, 2016; published online February 3, 2017. Assoc. Editor: Kunio Hasegawa.
- Views Icon Views
- Share Icon Share
- Search Site
Park, D., and Gravel, J. (February 3, 2017). "Effects of Loading Mode on Brittle Fracture of X70 Pipe Girth Welds." ASME. J. Pressure Vessel Technol. June 2017; 139(3): 031403. https://doi.org/10.1115/1.4035272
Download citation file: